Super Alloy HASTELLOY(r) C276 (UNS N10276) 6.35*1.65 mm

Short Description:

Chemical Composition

Super Alloy HASTELLOY(r) C276 (UNS N10276) 6.35*1.65 mm

The chemical composition of HASTELLOY(r) C276 is outlined in the following table.

Element Content (%)
Nickel, Ni 57
Molybdenum, Mo 15-17
Chromium, Cr 14.5-16.5
Iron, Fe 4-7
Tungsten, W 3-4.50
Cobalt, Co  2.50
Manganese, Mn  1
Vanadium, V  0.35
Silicon, Si  0.080
Phosphorous, P  0.025
Carbon, C  0.010
Sulfur, S  0.010

Physical Properties

Super Alloy HASTELLOY(r) C276 (UNS N10276) 6.35*1.65 mm

The following table shows the physical properties of HASTELLOY(r) C276.

Properties Metric Imperial
Density 8.89 g/cm³ 0.321 lb/in³
Melting point 1371°C 2500°F

Mechanical Properties

Super Alloy HASTELLOY(r) C276 (UNS N10276) 6.35*1.65 mm

The mechanical properties of HASTELLOY(r) C276 are displayed in the following table.

Properties Metric Imperial
Tensile strength (@thickness 4.80-25.4 mm, 538°C/@thickness 0.189-1.00 in, 1000°F) 601.2 MPa 87200 psi
Yield strength (0.2% offset, @thickness 2.40 mm, 427°C/@thickness 0.0945 in, 801°F) 204.8 MPa 29700 psi
Elastic modulus (RT) 205 GPa 29700 ksi
Elongation at break (in 50.8 mm, @thickness 1.60-4.70 mm, 204°C/@thickness 0.0630-0.185 in, 399°F) 56% 56%
Hardness, Rockwell B (plate) 87 87

Thermal Properties

The thermal properties of HASTELLOY(r) C276 are given in the following table.

Properties Metric Imperial
Thermal expansion co-efficient (@24-93°C/75.2-199°F) 11.2 µm/m°C 6.22 µin/in°F
Thermal conductivity (-168 °C) 7.20 W/mK 50.0 BTU in/hr.ft².°F

Other Designations

Equivalent materials to HASTELLOY(r) C276 are as follows.

ASTM B366 ASTM B574 ASTM B622 ASTM F467 DIN 2.4819
ASTM B575 ASTM B626 ASTM B619 ASTM F468  
         

Product Detail

Product Tags

Chemical Composition

Super Alloy HASTELLOY(r) C276 (UNS N10276) 6.35*1.65 mm

The chemical composition of HASTELLOY(r) C276 is outlined in the following table.

Element Content (%)
Nickel, Ni 57
Molybdenum, Mo 15-17
Chromium, Cr 14.5-16.5
Iron, Fe 4-7
Tungsten, W 3-4.50
Cobalt, Co  2.50
Manganese, Mn  1
Vanadium, V  0.35
Silicon, Si  0.080
Phosphorous, P  0.025
Carbon, C  0.010
Sulfur, S  0.010

Physical Properties

Super Alloy HASTELLOY(r) C276 (UNS N10276) 6.35*1.65 mm

The following table shows the physical properties of HASTELLOY(r) C276.

Properties Metric Imperial
Density 8.89 g/cm³ 0.321 lb/in³
Melting point 1371°C 2500°F

Mechanical Properties

Super Alloy HASTELLOY(r) C276 (UNS N10276) 6.35*1.65 mm

The mechanical properties of HASTELLOY(r) C276 are displayed in the following table.

Properties Metric Imperial
Tensile strength (@thickness 4.80-25.4 mm, 538°C/@thickness 0.189-1.00 in, 1000°F) 601.2 MPa 87200 psi
Yield strength (0.2% offset, @thickness 2.40 mm, 427°C/@thickness 0.0945 in, 801°F) 204.8 MPa 29700 psi
Elastic modulus (RT) 205 GPa 29700 ksi
Elongation at break (in 50.8 mm, @thickness 1.60-4.70 mm, 204°C/@thickness 0.0630-0.185 in, 399°F) 56% 56%
Hardness, Rockwell B (plate) 87 87

Thermal Properties

The thermal properties of HASTELLOY(r) C276 are given in the following table.

Properties Metric Imperial
Thermal expansion co-efficient (@24-93°C/75.2-199°F) 11.2 µm/m°C 6.22 µin/in°F
Thermal conductivity (-168 °C) 7.20 W/mK 50.0 BTU in/hr.ft².°F

Other Designations

Equivalent materials to HASTELLOY(r) C276 are as follows.

ASTM B366 ASTM B574 ASTM B622 ASTM F467 DIN 2.4819
ASTM B575 ASTM B626 ASTM B619 ASTM F468