317/317L stainless steel 6.35*0.70mm coiled tubing/straight tubing

Short Description:

The higher molybdenum content of Alloy 317L assures superior general and localized corrosion resistance in most media when compared with 304/304L and 316/316L stainless steels. Environments that don’t attack 304/304L stainless steel will normally not corrode 317L. One exception, however, are strongly oxidizing acids such as nitric acid. Alloys that contain molybdenum generally do not perform as well in these environments.

317/317L stainless steel 6.35*0.70mm coiled tubing/straight tubing

Alloy 317L has excellent corrosion resistance to a wide range of chemicals. It resists attack in sulfuric acid, acidic chlorine and phosphoric acid. It is used in handling hot organic and fatty acids often present in food and pharmaceutical processing applications.

The corrosion resistance of 317 and 317L should be the same in any given environment. The one exception is where the alloy will be exposed to temperatures in the chromium carbide precipitation range of 800 – 1500°F (427 – 816°C). Because of its low carbon content, 317L is the preferred material in this service to guard against intergranular corrosion.

317/317L stainless steel 6.35*0.70mm coiled tubing/straight tubing

In general, austenitic stainless steels are subject to chloride stress corrosion cracking in halide service. Although 317L is somewhat more resistant to stress corrosion cracking than 304/304L stainless steels, because of its higher molybdenum content, it is still susceptible.

317/317L stainless steel 6.35*0.70mm coiled tubing/straight tubing

The higher chromium, molybdenum and nitrogen content of 317L enhance its ability to resist pitting and crevice corrosion in the presence of chlorides and other halides. The Pitting Resistance Equivalent including Nitrogen number (PREN) is a relative measure of pitting resistance. The following chart offers a comparison Alloy 317L and other austenitic stainless steels.

ALLOY Composition (Weight Percent) PREN1
Cr Mo N
304 Stainless Steel 18.0 0.06 19.0
316 Stainless Steel 16.5 2.1 0.05 24.2
317L Stainless Steel 18.5 3.1 0.06 29.7
SSC-6MO 20.5 6.2 0.22 44.5

Product Detail

Product Tags

The higher molybdenum content of Alloy 317L assures superior general and localized corrosion resistance in most media when compared with 304/304L and 316/316L stainless steels. Environments that don’t attack 304/304L stainless steel will normally not corrode 317L. One exception, however, are strongly oxidizing acids such as nitric acid. Alloys that contain molybdenum generally do not perform as well in these environments.

317/317L stainless steel 6.35*0.70mm coiled tubing/straight tubing

Alloy 317L has excellent corrosion resistance to a wide range of chemicals. It resists attack in sulfuric acid, acidic chlorine and phosphoric acid. It is used in handling hot organic and fatty acids often present in food and pharmaceutical processing applications.

The corrosion resistance of 317 and 317L should be the same in any given environment. The one exception is where the alloy will be exposed to temperatures in the chromium carbide precipitation range of 800 – 1500°F (427 – 816°C). Because of its low carbon content, 317L is the preferred material in this service to guard against intergranular corrosion.

317/317L stainless steel 6.35*0.70mm coiled tubing/straight tubing

In general, austenitic stainless steels are subject to chloride stress corrosion cracking in halide service. Although 317L is somewhat more resistant to stress corrosion cracking than 304/304L stainless steels, because of its higher molybdenum content, it is still susceptible.

317/317L stainless steel 6.35*0.70mm coiled tubing/straight tubing

The higher chromium, molybdenum and nitrogen content of 317L enhance its ability to resist pitting and crevice corrosion in the presence of chlorides and other halides. The Pitting Resistance Equivalent including Nitrogen number (PREN) is a relative measure of pitting resistance. The following chart offers a comparison Alloy 317L and other austenitic stainless steels.

ALLOY Composition (Weight Percent) PREN1
Cr Mo N
304 Stainless Steel 18.0 0.06 19.0
316 Stainless Steel 16.5 2.1 0.05 24.2
317L Stainless Steel 18.5 3.1 0.06 29.7
SSC-6MO 20.5 6.2 0.22 44.5